TC11合金β相区大应变热变形行为及组织研究Investigation on hot deformation behavior and microstructure of TC11 alloy at large strain during β-phase
李鑫;赵为纲;鲁世强;王克鲁;
摘要(Abstract):
利用热模拟试验机,在温度为1020~1080℃和应变速率为0.001~70 s~(-1)范围内对TC11合金进行真应变为1.2的大应变等温恒应变速率压缩试验,获悉高温塑性流动的应力-应变关系曲线特征,并对变形前后的微观组织进行观察。结果表明:流动应力随应变速率升高和温度降低而增加,但前者比后者对流动应力的影响更为显著;在所研究的温度范围内,当应变速率大于10.0 s~(-1)时,变形组织主要为拉长的β晶粒;当应变速率在1.0~0.01 s~(-1)之间时,变形试样分别发生部分动态再结晶和完全动态再结晶;当应变速率为0.001 s~(-1)时,变形试样以动态回复为主。为获得良好的变形组织,热加工区域以温度在1020~1050℃,应变速率在0.01~1.0 s~(-1)范围为宜。
关键词(KeyWords): TC11合金;热态压缩;流动应力;微观组织;变形机制
基金项目(Foundation):
作者(Author): 李鑫;赵为纲;鲁世强;王克鲁;
Email:
DOI: 10.14024/j.cnki.1004-244x.2007.03.008
参考文献(References):
- [1]Ding R,Guo Z X,Wilson A.Microstructural evolution of a Ti- 6Al-4V alloy during thermomechanical processing[J].Mate- rials Science and Engineering,2002,A327:233-245.
- [2]王金友,葛志明,周彦邦.航空用钛合金[M].上海:上海科学技术出版社,1985:117.
- [3]李健,周义刚.TC11钛合金β锻造变形程度及其锻后热处理对组织性能的影响[J].机械工程材料,1998,24(2):22- 24.
- [4]周义刚,曾卫东,俞汉清.近β锻造推翻陈旧理论发展了三态组织[J].中国工程科学,2001,3(5):61-66.
- [5]杨觉先.金属塑性变形物理基础[M].北京:冶金工业出版社,1987:144.
- [6]王敏敏,赵永庆,周廉.Ti40阻燃钛合金的高温蠕变行为[J].稀有金属材料与工程,2003,32(2):117-120.
- [7]曾卫东,胡鲜红,俞汉清,等.Ti-17合金高温变形机理研究[J].材料工程,1996(9):27-30.
- [8]Seshacharyulu T,Medeiros S C,Frazier W G,et al.Hot working of commercial Ti-6Al-4V with an equiaxedα-βmicrostruc- ture:materials modeling considerations[J].Materials Science and Engineering,2000,A284:184-194.
- [9]冯亮,曲恒磊,赵永庆,等.TC21合金的高温变形行为[J].航空材料学报,2004,24(4):11-13.
- [10]鲍如强,黄旭,黄利军.Ti-IOV-2Fe-3Al合金热工艺的研究[J].稀有金属,2005,29(2):214-218.
- [11]Brun M,Anoshkin N,Shakhanova G.Physical processes and regimes of thermomechanical processing controlling development of regulated structure in theα+βtitanium alloys [J].Materials Science and Engineering,1998,A243:77-81.
- [12]王占学.塑性加工金属学[M].北京:冶金工业出版社, 1989:157.
- [13]Seshacharyulu T,Medeiros S C,Frazier W G,et al.Microstruc- tural mechanisms during hot working of commercial grade Ti-6Al-4V with lamellar starting structure[J].Materials Science and Engineering,2002,A325:112-125.
- [14]Ding R,Guo Z X.Microstructural evolution of a Ti-6Al-4V alloy duringβ-phase processing:experimental and simula- tive investigations[J].Materials Science and Engineering, 2004,A365:172-179.
- [15]Prasad Y V R K,Seshacharyulu T.Processing maps for hot working of titanium alloys[J].Materials Science and Enginee- ring,1998,A243:82-88.
- [16]Seshacharyulu T,Medeiros S C,Morgan J T,et al.Hot deformation and microstructural damage mechanisms in extra -low interstitial(ELI)grade Ti-6Al-4V[J].Materials Science and Engineering,2000,A279:289-299.