机械球磨法制备TiC/Al复合涂层的显微组织及力学性能Microstructure and mechanical properties of TiC/Al composite coating fabricated by high energy ball milling technique
孙斌斌;李玉芳;顾冬冬;
摘要(Abstract):
采用高能球磨机,室温下在2024铝合金表面制得TiC/Al复合涂层。利用SEM,XRD、显微硬度测试和摩擦磨损测试等技术分析涂层的显微形貌、组织结构及力学性能并初步探讨涂层的形成机理。结果表明,在350r/min转速下球磨3h后,2024铝合金表面形成界面结合良好且平均厚度为20μm的TiC/Al复合涂层。涂层最大显微硬度值高达314HV0.1,是基体硬度值的2倍多。界面处的显微硬度呈现梯度变化,对合金层起到很好的缓冲和支撑作用。摩擦磨损测试表明,涂层有效地降低原有材料的摩擦因数,使其耐磨性得到一定程度的提高。
关键词(KeyWords): 高能球磨;TiC/Al复合涂层;界面;显微硬度
基金项目(Foundation):
作者(Author): 孙斌斌;李玉芳;顾冬冬;
Email:
DOI: 10.14024/j.cnki.1004-244x.2010.01.006
参考文献(References):
- [1]Komarov Sergey V,Son Sang H,Hayashi Naohito,et al.De-velopment of a novel method for mechanical plating using ul-trasonic vibrations[J].Surface&Coatings Technology,2007,201(16/17):6999-7006.
- [2]Revesz A,Takacs L.Coating metals by surface mechanical attrition treatment[J].Journal of Alloys and Compounds,2007,441(1/2):111-114.
- [3]Zhan Zhaolin,He Yedong,Wang Deren,et al.Low-temperature processing of Fe-Al intermetallic coatings assisted by ball milling[J].Intermetallics,2006,14(1):75-81.
- [4]Romankov S,Sha W,Kaloshkin S D,et al.Fabrication of Ti-Al coatings by mechanical alloying method[J].Surface and Coat-ings Technology,2006,201(6):3235-3245.
- [5]Komarov Sergey V,Romankov Sergey E,Son Sang Han,et al.Production of LaPO4coatings using a novel ultrasonically-as-sisted plating technique[J].Surface&Coatings Technology,2008,202(21):5180-5184.
- [6]Romankov S,Komarov S V,Vdovichenko E.Fabrication of TiN coatings using mechanical milling techniques[J].Int Journal of Refractory Metals&Hard Materials,2009,27(2):492-497.
- [7]Romankov S,Hayasaka Y,Kalikova G,et al.TEM study of TiN coatings fabricated by mechanical milling using vibration technique[J].Surface&Coatings Technology,2009,203(13):1879-1884.
- [8]Takacs Laszlo,Torosyan Aghasi R.Surface mechanical alloy-ing of an aluminum plate[J].Journal of Alloys and Com-pounds,2007,434/435:686-688.
- [9]Zhan Zhaolin,He Yedong,Wang Deren,et al.Preparation of aluminide coatings at relatively low temperatures[J].Transac-tions of Nonferrous Metals Society of China,2006,16(3):647-653.