高速铣削参数对超高强度钢表面完整性影响研究Effect of high-speed milling parameters on surface integrity of ultra-high strength steel
杨振朝;薛阳;袁启龙;徐瑾;李言;
摘要(Abstract):
为有效控制超高强度钢高速铣削加工过程中的表面完整性,利用涂层硬质合金刀片对16Co14Ni10Cr2Mo超高强度钢进行高速铣削试验。研究铣削速度、每齿进给量和铣削深度对三维表面形貌、三维表面粗糙度和表面残余应力的影响规律。通过3D共聚焦轮廓显微测量仪和X射线衍射仪对加工后的三维表面形貌、三维表面粗糙度和表面残余应力进行测试分析。结果表明:三维表面形貌图中等距纹理为铣削参数中每齿进给量的体现,三维表面形貌与三维表面粗糙度之间具有映射关系;三维表面粗糙度随铣削速度的增大呈下降趋势,随每齿进给量和铣削深度的增大而增大,每齿进给量影响最为显著;在试验参数范围内,表面残余应力均为拉应力,随铣削速度的增大,x向表面残余应力呈上升趋势,y向表面残余应力呈下降趋势;随每齿进给量的增大,x向和y向表面残余应力均呈上升趋势;随铣削深度的增大,x向和y向表面残余应力变化不明显。
关键词(KeyWords): 超高强度钢;三维表面形貌;三维表面粗糙度;表面残余应力;铣削参数
基金项目(Foundation): 国家自然科学基金(51775431;51475367);; 陕西省科技统筹创新工程计划(2014SZS10-Z01)
作者(Author): 杨振朝;薛阳;袁启龙;徐瑾;李言;
Email:
DOI: 10.14024/j.cnki.1004-244x.20180816.002
参考文献(References):
- [1]赵博,许广兴,贺飞,等.飞机起落架用超高强度钢应用现状及展望[J].航空材料学报,2017,37(6):1-6.
- [2]REMES H,KORHONEN E,LEHTO P,et al. Influence of sur-face integrity on the fatigue strength of high-strength steels[J].Journal of Constructional Steel Research,2013,89:21-29.
- [3]刘彦臣,庞思勤,王西彬,等.表面完整性对高强度钢疲劳寿命影响的试验研究[J].兵工学报,2013,34(6):759-764.
- [4]岳彩旭,刘献礼.高强度钢已加工表面完整性的研究进展[J].哈尔滨理工大学学报,2012,16(6):5-10.
- [5]张慧萍,刘壬航,李珍灿,等. 300 M超高强度钢高速切削过程仿真研究[J].机械科学与技术,2017,36(10):1550-1555.
- [6]苏永生,李亮,王建彬,等.超硬织构化刀具高速切削钛合金试验研究[J].表面技术,2018,47(2):249-254.
- [7]谭靓,张定华,姚倡锋.高速铣削参数对TC17钛合金表面变质层的影响[J].航空材料学报,2017,37(6):75-81.
- [8]ZHOU N,PENG R L,PETTERSSON R. Surface integrity of2304 duplex stainless steel after different grinding operations[J]. Journal of Materials Processing Technology,2016,229:294-304.
- [9]LIU G,HUANG C,ZOU B,et al. Surface integrity and fatigueperformance of 17-4PH stainless steel after cutting operations[J]. Surface&Coatings Technology,2016,307:182-189.
- [10]MU?OZ E P,SHOKRANI A,NEWMANB S T. Influence ofcutting environments on surface integrity and power consump-tion of austenitic stainless steel[J]. Robotics and Computer-Integrated Manufacturing,2015,36:60-69.
- [11]CHINCHANIKAR S,CHOUDHURY S K. Effect of work ma-terial hardness and cutting parameters on performance of coat-ed carbide tool when turning hardened steel:An optimizationapproach[J]. Journal of Materials Processing Technology,2012,67:55-61.
- [12]SONG G,LI J,SUN J,et al. The influence of milling parame-ters on surface residual stresses during milling AF1410 ultra-high strength steel[J]. Key Engineering Materials,2010,431/432:209-212.
- [13]罗智文,焦黎,赵文祥,等. 58SiMn高强度钢车削表面完整性的实验研究[J].表面技术,2017,46(1):234-240.
- [14]郭伟刚,赵从容,吴晓苏,等.干式磨削ANSID2淬硬模具钢的表面完整性试验研究[J].中国机械工程,2015,26(16):2134-2142.
- [15]文武,万翛如. 16Co14Ni10Cr2Mo钢冲击裂纹的形成和扩展机制[J].航空材料学报,1997,17(1):39-43.